Density: 15,20 g/cm3
Hardness (as cast): 145 HV
Hardness (after cold work 70%): 258 HV
Hardness (after annealing): 136 HV
Hardness (after age hardening): 225 HV
DIRECTIONS FOR SUGGESTED USE
Melting temperature: 900 °C
Casting temperature:
100 °C over its melting temperature to cast into ingot-mould and continuous casting.
100 °C over its melting temperature to cast with centrifugal machines.
120 °C over its melting temperature to cast in vacuum machines with controlled atmosphere.
140 °C over its melting temperature to cast in outdoor cylinders with vacuum.
Ingot-mould temperature: 150 °C
Cylinders temperature: from 550 °C to 650 °C depending on the machine and
objects dimensions.
Cooling of ingots: quick in lukewarm water (about 40 °C)
Cooling casted objects: in water after 10 minutes.
Cooling casted objects (with stone): in water after 30/40 minutes.
Annealing: 650 °C for 20 minutes followed by a quick cooling in hot
water (40 °C min.)
Age hardening: Step 1: solubilization
680 °C for 30 minutes. Cooling quickly in warm water
(about 40 °C).
Step 2: hardening
300 °C for 2 hours. Cooling at room temperature